FLOW CONTROL REFRACTORIES
|
|
|
SLIDE
GATE REFRACTORIES
| Product | A.P.* % | B.D* (gm/cc) | Al2O3 % | Fe2O3 % | Cr2O3 % | MgO % | F.C % | ZrO2 % | HMOR 1400oC (kg/cm2) | Application Area |
|
SLIDE PLATE : |
||||||||||
| CC-SP-98-M | 17 | 2.95 | - | - | - | 97 | - | - | - | Continuous casting |
| CC-SP-85-CA | 16 | 3.10 | 84 | - | - | - | 4 | - | - | Ingot & Continuous casting |
| CC-SP-85-CAS | 16 | 3.00 | 80 | - | - | - | 4 | 5.5 | - | Continuous casting |
| CC-SP-85-CASS |
16 |
3.00 | 72 | - | - | - | 4 | 9.0 | - | Continuous casting |
| CC-AZC | 6 | 3.00 | 75 | - | - | - | 4 | 9.0 | 150 | Continuous casting |
| CC-SPSR | 8 | 2.80 | - | - | - | 80 | - | - | 100 | Continuous casting |
|
NOZZLE |
||||||||||
| CC-SN-90-C | 20 | 3.00 | 88 | 0.5 | 3 | - | - | - | - | Nozzle for slide gate system |
| CC-SN-85-F | 20 | 2.95 | 84 | 0.5 | - | - | - | - | - | Nozzle for slide gate system |
| CC-SN-85-CA | 18 | 2.95 | 84 | - | - | - | 4 | - | - | Nozzle for slide gate system |
| CC-SN-90-CA | 12 | 2.90 | 90 | - | - | - | 2 | - | - | Nozzle for slide gate system |
| CC-SN-90-M | 12 | 2.90 | - | - | - | 90 | 5 | - | - | Nozzle for slide gate system |
|
WELL BLOCK/SEATING BLOCK : |
||||||||||
| CC-SW-98-T | - | 3.00 | 98 | - | - | - | - | - | - | Well block/Seating Block |
| CC-SW-ULCC-75 | - | 2.75 | 75 | 0.7 | - | - | - | - | - | Well block/Seating Block |
Properties before pitch impregnation
| Product | A.P.* % | B.D* (gm/cc) | Al2O3 % | Fe2O3 % | MgO % |
Air Flow at 0.4 kg/cm2
Ltrs/min |
Application Area |
|
POROUS PLUG : |
|||||||
| CC-PP (Part-1) | 18 | - | 88 | - | - | 50 | Steel Ladle, LRF, VOD |
| CC-PP (Part-2) | 23-30 | - | - | - | 95 | - | Steel Ladle, LRF, VOD |
| CC-MPP (1) | 23-30 | - | - | - | 95 | 30 | Steel Ladle, LRF, VOD |